1.Kristalex™ 5140

Hydrocarbon Resin

Application/Uses

Alluminum-pigment preparations

Assembly

Automotive

Building and Construction

Caulks and Sealants

Hot Melt Adhesives

Laminating

Nonwovens

Pressure sensitive adhesives

Rubber and Plastic Modification

Solventborne Adhesives

Tapes and Labels

Product Description

Kristalex™ 5140 hydrocarbon resin is a high

softening point, low molecular weight resin

produced by copolymerization of pure aromatic

monomers. It is designed primarily for use as a

modifier resin in high performance adhesives and

coating compositions. In these applications,

its water clear color, heat stability, and

resistance to oxidation and discoloration are used to

advantage. In EVA-based hot melt adhesives,

Kristalex™ 5140 is compatible with EVA grades

with up to 18% vinyl acetate and is useful in

formulating low-color adhesives with improved

high temperature resistance. In styrenic block

copolymer based adhesives,

Kristalex™F100单体树脂产品描述

Kristalex™F100烃类树脂是一种水清，颜色稳定，低分子量

热塑性烃聚合物。由纯化的8 - 9个碳芳香单体组成

树脂用于塑料改性，热熔粘合剂和涂料，密封剂

和填缝材料。Kristalex™F100是兼容各种油，蜡，醇酸，塑料，

和弹性体，并可溶于许多常见的有机溶剂。基于eva的热熔体

Kristalex™F100粘合剂兼容EVA等级与高达18%的醋酸乙烯酯和is

适用于制备低温性能良好的低颜色胶粘剂。在苯乙烯

嵌段共聚物粘合剂Kristalex™F100优先与苯乙烯结合

端块，产生更高的室温内聚力，而不影响粘着力和附着力

属性。 浙江原装进口伊斯曼单体树脂Piccolastic D125特点：水白色，抗氧化稳定、热稳定性好。用于嵌段聚合物和EVA及羧化聚苯乙烯丁二烯的增粘,同时加强耐热性。

Kristalex™ F115 兼容性和溶解度

兼容于所有比例，或有限但实际有用的比例，与各种各样的

材料如SIS(苯乙烯-异戊二烯-苯乙烯)，SBS(苯乙烯-丁二烯-苯乙烯)和SEBS

(苯乙烯-乙烯-丁二烯-苯乙烯)嵌段共聚物、氯丁烯、丁腈、聚丁二烯、

丙烯酸类聚合物、氯化橡胶、EVA树脂(乙烯-醋酸乙烯共聚物)、

苯乙烯化醇酸，乙烯化醇酸，干油醇酸，松香酯树脂。

溶于芳香烃、氯代烃、酮、醚。不溶性是脂肪族

碳氢化合物、醇和乙二醇。

包装

多层纸袋装(净重20公斤)，每托盘50袋。

Piccotex™LC单体树脂产品描述

Piccotex™LC烃树脂是一系列高软化点树脂中的一员

稳定、热塑性材料基于纯化的芳香单体，具有稍宽的应用范围

颜色规格比其他Piccotex™产品。这些树脂具有优异的热粘性;

热密封性能;抗变色;耐酸碱、耐潮湿;和稳定性

在混合过程中遇到的温度升高。高初始和保留光泽，和

提高卷帘涂布和卷帘涂布设备的应用速度。Piccotex™LC

与食品直接接触的应用符合FDA的一些规定。

在a中使用之前，应验证特定情况下给定法规的符合性

食品接触应用。

兼容性和溶解度

与石蜡、氯化石蜡、微晶蜡的有效比例相容，含量低

分子量聚乙烯，高苯乙烯树脂，乙烯-甲苯聚合物，乙烯-乙烯

醋酸酯(EVA)共聚物和许多常见的增塑剂。溶于脂肪族、芳香族和

氯化碳氢化合物;醚;酯;硝基烷;和苯甲醇。不溶于低

醇类，二醇类和水。对于低挥发性有机化合物或零挥发性有机化合物系统，Piccotex™可溶于挥发性有机化合物中

免除溶剂乙酸t-丁酯和高氯苯四氟化(PCBTF)，并可耐受

在以TBA和/或TBA为基础的溶剂体系中作为稀释剂的**和/或乙酸甲酯

PCBTF。VOC的豁免和环境法规因地区而异

在对VOC含量提出任何索赔之前，应核实当地标准。 单体树脂在免钉胶里面的应用。

Kristalex™ 1120 Hydrocarbon Resin

应用程序/使用

压敏胶粘剂

橡胶和塑料改性

粘合剂

磁带和唱片公司

关键属性

优异的热稳定性水白色初始色

Typical

Properties产品指标

Property                   Test Method   Typical Value, Units

Ring

and Ball Softening Point ASTM E 28   119°C

Color

a YID                                 7

Cloud

Point b

MMAP                                      5°C

DACP                                      -35°C

OMS                                       >180°C

Molecular

Weight c

Mz                                                7600

Melt

Viscosity

1

poise                               235°C

(455°F)

10

poise                              195°C (385°F)

100

poise                             160°C

(320°F)

1000

poise                            140°C

(285°F)

aGlass Transition Temperature (Tg) d                  60°C

关键属性

优异的热稳定性水白色初始色

Kristalex 3085单体树脂低软化点，现货供应，塑料改性，TPE改性。安徽原厂原包伊斯曼单体树脂Kristalex F115

属性                  测试方法              典型值 单位

环球软化点            ASTM E 28            139°C

颜色黄色指数                                 4

雾点

MMAP                                       9°C

DACP                                    

 -48°C

OMS                                        >180°C

分子量

Mz                                                  12100

熔融粘度

10

poise                                     220°C

100

poise                                    180°C

1000

poise                                   160°C

玻璃化温度                                    85°C

Typical

Properties

Property                   Test Method   Typical Value, Units

Ring

and Ball Softening Point ASTM E 28   139°C

Color

a YID                                 4

Cloud

Point b

MMAP                                      9°C

DACP                                      -48°C

OMS                                       >180°C

Molecular

Weight c

Mz                                                12100

Melt

Viscosity

10

poise                                          220°C

100

poise                                         180°C

1000

poise                                        160°C

Glass

Transition Temperature (Tg) d                  85°C